{"title":"DIN 6798J Zinc Internal Serrated Lock","description":"\u003ch1\u003eDIN 6798J Internal Serrated Lock Washer — 65Mn Spring Steel, Zinc Plated CR3\u003c\/h1\u003e\n\n\u003cp\u003eFULLERKREG DIN 6798J internal serrated lock washers are manufactured to DIN 6798 Form J standard in 65Mn high-manganese spring steel (per GB\/T 1222) with zinc electroplating and trivalent chromium (CR3) passivation. DIN 6798 Form J features internal serrations (teeth on the inner diameter) that bite into the fastener shank or bolt head bearing surface, providing positive anti-loosening performance through mechanical engagement while preserving the outer substrate surface. 65Mn spring steel achieves 430–510 HV hardness after quench and temper, delivering superior tooth sharpness retention and fatigue resistance. The zinc CR3 finish provides ≥72h salt spray resistance with full RoHS compliance.\u003c\/p\u003e\n\n\u003cp\u003e\u003cstrong\u003eNote on hydrogen embrittlement:\u003c\/strong\u003e At 430–510 HV, electroplating introduces hydrogen embrittlement risk. FULLERKREG applies mandatory post-plate baking (per ISO 9587 \/ GB\/T 13912) to eliminate this risk and ensure tooth integrity.\u003c\/p\u003e\n\n\u003chr\u003e\n\n\u003ch2\u003eProduct Highlights\u003c\/h2\u003e\n\u003cul\u003e\n  \u003cli\u003e\n\u003cstrong\u003eStandard:\u003c\/strong\u003e DIN 6798 Form J (Internal Serrated Lock Washer)\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eMaterial:\u003c\/strong\u003e 65Mn Spring Steel (GB\/T 1222)\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eSurface Treatment:\u003c\/strong\u003e Zinc Electroplating + CR3 Trivalent Chromium Passivation\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eCorrosion Resistance:\u003c\/strong\u003e ≥72h neutral salt spray (NSS) per ISO 9227\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eHardness:\u003c\/strong\u003e 430–510 HV (approx. 44–50 HRC) after quench \u0026amp; temper\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eSize Range:\u003c\/strong\u003e M3 – M30\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eSerration type:\u003c\/strong\u003e Internal (teeth on inner diameter — bite into fastener shank)\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eOuter surface preserved\u003c\/strong\u003e — no marking on substrate outer surface\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eRoHS Compliant\u003c\/strong\u003e — CR3, no Cr6+\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003ePost-plate baking\u003c\/strong\u003e — hydrogen embrittlement relief per ISO 9587\u003c\/li\u003e\n\u003c\/ul\u003e\n\n\u003chr\u003e\n\n\u003ch2\u003eDimensional Specifications — DIN 6798 Form J (Internal Serrated), 65Mn Steel Zinc CR3\u003c\/h2\u003e\n\u003cp\u003eAll dimensions in millimeters (mm). Per DIN 6798 Form J.\u003c\/p\u003e\n\n\u003ctable\u003e\n  \u003cthead\u003e\n    \u003ctr\u003e\n\u003cth\u003eFor Thread\u003c\/th\u003e\n\u003cth\u003eNominal Size\u003c\/th\u003e\n\u003cth\u003ed1 min\u003c\/th\u003e\n\u003cth\u003ed1 max\u003c\/th\u003e\n\u003cth\u003ed2 Nominal\u003c\/th\u003e\n\u003cth\u003ed3 approx.\u003c\/th\u003e\n\u003cth\u003eMin. No. of Teeth\u003c\/th\u003e\n\u003cth\u003es min\u003c\/th\u003e\n\u003cth\u003es max\u003c\/th\u003e\n\u003cth\u003ekg\/1000pcs\u003c\/th\u003e\n\u003c\/tr\u003e\n  \u003c\/thead\u003e\n  \u003ctbody\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM3\u003c\/td\u003e\n\u003ctd\u003e3\u003c\/td\u003e\n\u003ctd\u003e3.2\u003c\/td\u003e\n\u003ctd\u003e3.5\u003c\/td\u003e\n\u003ctd\u003e6.5\u003c\/td\u003e\n\u003ctd\u003e5.3\u003c\/td\u003e\n\u003ctd\u003e9\u003c\/td\u003e\n\u003ctd\u003e0.3\u003c\/td\u003e\n\u003ctd\u003e0.4\u003c\/td\u003e\n\u003ctd\u003e0.025\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM3.5\u003c\/td\u003e\n\u003ctd\u003e3.5\u003c\/td\u003e\n\u003ctd\u003e3.7\u003c\/td\u003e\n\u003ctd\u003e4.0\u003c\/td\u003e\n\u003ctd\u003e7.5\u003c\/td\u003e\n\u003ctd\u003e6.0\u003c\/td\u003e\n\u003ctd\u003e9\u003c\/td\u003e\n\u003ctd\u003e0.3\u003c\/td\u003e\n\u003ctd\u003e0.4\u003c\/td\u003e\n\u003ctd\u003e0.04\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM4\u003c\/td\u003e\n\u003ctd\u003e4\u003c\/td\u003e\n\u003ctd\u003e4.3\u003c\/td\u003e\n\u003ctd\u003e4.6\u003c\/td\u003e\n\u003ctd\u003e8.0\u003c\/td\u003e\n\u003ctd\u003e6.5\u003c\/td\u003e\n\u003ctd\u003e11\u003c\/td\u003e\n\u003ctd\u003e0.4\u003c\/td\u003e\n\u003ctd\u003e0.5\u003c\/td\u003e\n\u003ctd\u003e0.06\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM5\u003c\/td\u003e\n\u003ctd\u003e5\u003c\/td\u003e\n\u003ctd\u003e5.3\u003c\/td\u003e\n\u003ctd\u003e5.6\u003c\/td\u003e\n\u003ctd\u003e9.5\u003c\/td\u003e\n\u003ctd\u003e7.7\u003c\/td\u003e\n\u003ctd\u003e11\u003c\/td\u003e\n\u003ctd\u003e0.5\u003c\/td\u003e\n\u003ctd\u003e0.6\u003c\/td\u003e\n\u003ctd\u003e0.1\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM6\u003c\/td\u003e\n\u003ctd\u003e6\u003c\/td\u003e\n\u003ctd\u003e6.4\u003c\/td\u003e\n\u003ctd\u003e6.8\u003c\/td\u003e\n\u003ctd\u003e11.5\u003c\/td\u003e\n\u003ctd\u003e9.3\u003c\/td\u003e\n\u003ctd\u003e14\u003c\/td\u003e\n\u003ctd\u003e0.5\u003c\/td\u003e\n\u003ctd\u003e0.6\u003c\/td\u003e\n\u003ctd\u003e0.17\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM7\u003c\/td\u003e\n\u003ctd\u003e7\u003c\/td\u003e\n\u003ctd\u003e7.4\u003c\/td\u003e\n\u003ctd\u003e7.8\u003c\/td\u003e\n\u003ctd\u003e13.0\u003c\/td\u003e\n\u003ctd\u003e10.5\u003c\/td\u003e\n\u003ctd\u003e14\u003c\/td\u003e\n\u003ctd\u003e0.5\u003c\/td\u003e\n\u003ctd\u003e0.6\u003c\/td\u003e\n\u003ctd\u003e0.24\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM8\u003c\/td\u003e\n\u003ctd\u003e8\u003c\/td\u003e\n\u003ctd\u003e8.4\u003c\/td\u003e\n\u003ctd\u003e8.8\u003c\/td\u003e\n\u003ctd\u003e15.0\u003c\/td\u003e\n\u003ctd\u003e12.1\u003c\/td\u003e\n\u003ctd\u003e14\u003c\/td\u003e\n\u003ctd\u003e0.6\u003c\/td\u003e\n\u003ctd\u003e0.8\u003c\/td\u003e\n\u003ctd\u003e0.38\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM10\u003c\/td\u003e\n\u003ctd\u003e10\u003c\/td\u003e\n\u003ctd\u003e10.5\u003c\/td\u003e\n\u003ctd\u003e11.0\u003c\/td\u003e\n\u003ctd\u003e18.0\u003c\/td\u003e\n\u003ctd\u003e14.6\u003c\/td\u003e\n\u003ctd\u003e16\u003c\/td\u003e\n\u003ctd\u003e0.8\u003c\/td\u003e\n\u003ctd\u003e1.0\u003c\/td\u003e\n\u003ctd\u003e0.7\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM12\u003c\/td\u003e\n\u003ctd\u003e12\u003c\/td\u003e\n\u003ctd\u003e13.0\u003c\/td\u003e\n\u003ctd\u003e13.5\u003c\/td\u003e\n\u003ctd\u003e21.0\u003c\/td\u003e\n\u003ctd\u003e17.0\u003c\/td\u003e\n\u003ctd\u003e18\u003c\/td\u003e\n\u003ctd\u003e0.8\u003c\/td\u003e\n\u003ctd\u003e1.0\u003c\/td\u003e\n\u003ctd\u003e0.9\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM14\u003c\/td\u003e\n\u003ctd\u003e14\u003c\/td\u003e\n\u003ctd\u003e15.0\u003c\/td\u003e\n\u003ctd\u003e15.5\u003c\/td\u003e\n\u003ctd\u003e24.0\u003c\/td\u003e\n\u003ctd\u003e19.5\u003c\/td\u003e\n\u003ctd\u003e18\u003c\/td\u003e\n\u003ctd\u003e0.8\u003c\/td\u003e\n\u003ctd\u003e1.0\u003c\/td\u003e\n\u003ctd\u003e1.2\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM16\u003c\/td\u003e\n\u003ctd\u003e16\u003c\/td\u003e\n\u003ctd\u003e17.0\u003c\/td\u003e\n\u003ctd\u003e17.5\u003c\/td\u003e\n\u003ctd\u003e27.0\u003c\/td\u003e\n\u003ctd\u003e21.9\u003c\/td\u003e\n\u003ctd\u003e18\u003c\/td\u003e\n\u003ctd\u003e1.0\u003c\/td\u003e\n\u003ctd\u003e1.2\u003c\/td\u003e\n\u003ctd\u003e1.9\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM18\u003c\/td\u003e\n\u003ctd\u003e18\u003c\/td\u003e\n\u003ctd\u003e19.0\u003c\/td\u003e\n\u003ctd\u003e19.5\u003c\/td\u003e\n\u003ctd\u003e30.0\u003c\/td\u003e\n\u003ctd\u003e24.4\u003c\/td\u003e\n\u003ctd\u003e18\u003c\/td\u003e\n\u003ctd\u003e1.0\u003c\/td\u003e\n\u003ctd\u003e1.2\u003c\/td\u003e\n\u003ctd\u003e2.3\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM20\u003c\/td\u003e\n\u003ctd\u003e20\u003c\/td\u003e\n\u003ctd\u003e21.0\u003c\/td\u003e\n\u003ctd\u003e21.5\u003c\/td\u003e\n\u003ctd\u003e33.0\u003c\/td\u003e\n\u003ctd\u003e26.8\u003c\/td\u003e\n\u003ctd\u003e20\u003c\/td\u003e\n\u003ctd\u003e1.0\u003c\/td\u003e\n\u003ctd\u003e1.2\u003c\/td\u003e\n\u003ctd\u003e3.0\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM22\u003c\/td\u003e\n\u003ctd\u003e22\u003c\/td\u003e\n\u003ctd\u003e23.0\u003c\/td\u003e\n\u003ctd\u003e23.5\u003c\/td\u003e\n\u003ctd\u003e36.0\u003c\/td\u003e\n\u003ctd\u003e29.3\u003c\/td\u003e\n\u003ctd\u003e20\u003c\/td\u003e\n\u003ctd\u003e1.0\u003c\/td\u003e\n\u003ctd\u003e1.2\u003c\/td\u003e\n\u003ctd\u003e3.7\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM24\u003c\/td\u003e\n\u003ctd\u003e24\u003c\/td\u003e\n\u003ctd\u003e25.0\u003c\/td\u003e\n\u003ctd\u003e25.5\u003c\/td\u003e\n\u003ctd\u003e39.0\u003c\/td\u003e\n\u003ctd\u003e31.7\u003c\/td\u003e\n\u003ctd\u003e20\u003c\/td\u003e\n\u003ctd\u003e1.2\u003c\/td\u003e\n\u003ctd\u003e1.5\u003c\/td\u003e\n\u003ctd\u003e5.5\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM27\u003c\/td\u003e\n\u003ctd\u003e27\u003c\/td\u003e\n\u003ctd\u003e28.0\u003c\/td\u003e\n\u003ctd\u003e28.5\u003c\/td\u003e\n\u003ctd\u003e44.0\u003c\/td\u003e\n\u003ctd\u003e35.8\u003c\/td\u003e\n\u003ctd\u003e20\u003c\/td\u003e\n\u003ctd\u003e1.2\u003c\/td\u003e\n\u003ctd\u003e1.5\u003c\/td\u003e\n\u003ctd\u003e7.0\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eM30\u003c\/td\u003e\n\u003ctd\u003e30\u003c\/td\u003e\n\u003ctd\u003e31.0\u003c\/td\u003e\n\u003ctd\u003e31.5\u003c\/td\u003e\n\u003ctd\u003e47.0\u003c\/td\u003e\n\u003ctd\u003e38.2\u003c\/td\u003e\n\u003ctd\u003e20\u003c\/td\u003e\n\u003ctd\u003e1.2\u003c\/td\u003e\n\u003ctd\u003e1.5\u003c\/td\u003e\n\u003ctd\u003e8.0\u003c\/td\u003e\n\u003c\/tr\u003e\n  \u003c\/tbody\u003e\n\u003c\/table\u003e\n\u003cp\u003e\u003cem\u003eAll dimensions in mm per DIN 6798 Form J. d1 = inner diameter; d2 = outer diameter; d3 = serration root diameter; s = thickness.\u003c\/em\u003e\u003c\/p\u003e\n\n\u003chr\u003e\n\n\u003ch2\u003eMaterial Properties — 65Mn Spring Steel (GB\/T 1222)\u003c\/h2\u003e\n\u003ctable\u003e\n  \u003cthead\u003e\u003ctr\u003e\n\u003cth\u003eProperty\u003c\/th\u003e\n\u003cth\u003eValue\u003c\/th\u003e\n\u003c\/tr\u003e\u003c\/thead\u003e\n  \u003ctbody\u003e\n    \u003ctr\u003e\n\u003ctd\u003eMaterial Grade\u003c\/td\u003e\n\u003ctd\u003e65Mn Spring Steel\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eGB Standard\u003c\/td\u003e\n\u003ctd\u003eGB\/T 1222, GB\/T 4354\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eC Content\u003c\/td\u003e\n\u003ctd\u003e0.62 – 0.70%\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eMn Content\u003c\/td\u003e\n\u003ctd\u003e0.90 – 1.20%\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eHeat Treatment\u003c\/td\u003e\n\u003ctd\u003eQuench \u0026amp; Temper\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eHardness\u003c\/td\u003e\n\u003ctd\u003e430–510 HV (approx. 44–50 HRC)\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eTensile Strength\u003c\/td\u003e\n\u003ctd\u003e1275 MPa min.\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eSurface Treatment\u003c\/td\u003e\n\u003ctd\u003eZinc Electroplating + CR3 Passivation\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eSalt Spray Resistance\u003c\/td\u003e\n\u003ctd\u003e≥72h NSS per ISO 9227\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eH2 Embrittlement Relief\u003c\/td\u003e\n\u003ctd\u003ePost-plate baking per ISO 9587 \/ GB\/T 13912\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eOperating Temperature\u003c\/td\u003e\n\u003ctd\u003e-40°C to +120°C\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eRoHS \/ REACH\u003c\/td\u003e\n\u003ctd\u003eCompliant — CR3, no Cr6+\u003c\/td\u003e\n\u003c\/tr\u003e\n  \u003c\/tbody\u003e\n\u003c\/table\u003e\n\n\u003chr\u003e\n\n\u003ch2\u003eChemical Composition — 65Mn Spring Steel (GB\/T 1222)\u003c\/h2\u003e\n\u003ctable\u003e\n  \u003cthead\u003e\u003ctr\u003e\n\u003cth\u003eElement\u003c\/th\u003e\n\u003cth\u003eC\u003c\/th\u003e\n\u003cth\u003eMn\u003c\/th\u003e\n\u003cth\u003eSi\u003c\/th\u003e\n\u003cth\u003eP max\u003c\/th\u003e\n\u003cth\u003eS max\u003c\/th\u003e\n\u003cth\u003eCr max\u003c\/th\u003e\n\u003cth\u003eNi max\u003c\/th\u003e\n\u003c\/tr\u003e\u003c\/thead\u003e\n  \u003ctbody\u003e\n    \u003ctr\u003e\n\u003ctd\u003eContent %\u003c\/td\u003e\n\u003ctd\u003e0.62–0.70\u003c\/td\u003e\n\u003ctd\u003e0.90–1.20\u003c\/td\u003e\n\u003ctd\u003e0.17–0.37\u003c\/td\u003e\n\u003ctd\u003e0.035\u003c\/td\u003e\n\u003ctd\u003e0.035\u003c\/td\u003e\n\u003ctd\u003e0.25\u003c\/td\u003e\n\u003ctd\u003e0.25\u003c\/td\u003e\n\u003c\/tr\u003e\n  \u003c\/tbody\u003e\n\u003c\/table\u003e\n\n\u003chr\u003e\n\n\u003ch2\u003eDIN 6798 Form J vs. Form A — Key Differences\u003c\/h2\u003e\n\u003ctable\u003e\n  \u003cthead\u003e\u003ctr\u003e\n\u003cth\u003eFeature\u003c\/th\u003e\n\u003cth\u003eForm J (Internal) — This Product\u003c\/th\u003e\n\u003cth\u003eForm A (External)\u003c\/th\u003e\n\u003c\/tr\u003e\u003c\/thead\u003e\n  \u003ctbody\u003e\n    \u003ctr\u003e\n\u003ctd\u003eSerration location\u003c\/td\u003e\n\u003ctd\u003eInner diameter\u003c\/td\u003e\n\u003ctd\u003eOuter diameter\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eBites into\u003c\/td\u003e\n\u003ctd\u003eFastener shank \/ bolt head\u003c\/td\u003e\n\u003ctd\u003eSubstrate surface\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eOuter surface\u003c\/td\u003e\n\u003ctd\u003ePreserved — no marking\u003c\/td\u003e\n\u003ctd\u003eMarked by teeth\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eAnti-loosening torque\u003c\/td\u003e\n\u003ctd\u003eStandard\u003c\/td\u003e\n\u003ctd\u003eMaximum (larger radius)\u003c\/td\u003e\n\u003c\/tr\u003e\n    \u003ctr\u003e\n\u003ctd\u003eBest for\u003c\/td\u003e\n\u003ctd\u003eVisible \/ finished surfaces\u003c\/td\u003e\n\u003ctd\u003eGeneral industrial assemblies\u003c\/td\u003e\n\u003c\/tr\u003e\n  \u003c\/tbody\u003e\n\u003c\/table\u003e\n\n\u003chr\u003e\n\n\u003ch2\u003eApplication Scenarios\u003c\/h2\u003e\n\u003cul\u003e\n  \u003cli\u003e\n\u003cstrong\u003eVisible or finished surfaces\u003c\/strong\u003e — internal teeth preserve outer substrate appearance\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eHeavy machinery \u0026amp; industrial equipment\u003c\/strong\u003e — high hardness teeth, outdoor corrosion protection\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eAutomotive manufacturing\u003c\/strong\u003e — chassis and body assemblies exposed to moisture\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eConstruction \u0026amp; steel structures\u003c\/strong\u003e — sheltered outdoor environments\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eAgricultural \u0026amp; mining equipment\u003c\/strong\u003e — high-vibration, humid conditions\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eElectrical enclosures \u0026amp; control panels\u003c\/strong\u003e — reliable anti-loosening with corrosion protection\u003c\/li\u003e\n  \u003cli\u003e\n\u003cstrong\u003eGeneral bolted assemblies\u003c\/strong\u003e — where RoHS-compliant zinc finish is required\u003c\/li\u003e\n\u003c\/ul\u003e\n\n\u003chr\u003e\n\n\u003ch2\u003eProduct Photo Gallery\u003c\/h2\u003e\n\u003cp\u003eFULLERKREG DIN 6798J Internal Serrated Lock Washer, 65Mn Spring Steel, Zinc CR3:\u003c\/p\u003e\n\u003ctable\u003e\n  \u003ctbody\u003e\n    \u003ctr\u003e\n      \u003ctd style=\"width:25%;text-align:center;padding:12px\"\u003e[ Photo 1 ]\u003c\/td\u003e\n      \u003ctd style=\"width:25%;text-align:center;padding:12px\"\u003e[ Photo 2 ]\u003c\/td\u003e\n      \u003ctd style=\"width:25%;text-align:center;padding:12px\"\u003e[ Photo 3 ]\u003c\/td\u003e\n      \u003ctd style=\"width:25%;text-align:center;padding:12px\"\u003e[ Photo 4 ]\u003c\/td\u003e\n    \u003c\/tr\u003e\n  \u003c\/tbody\u003e\n\u003c\/table\u003e\n\n\u003chr\u003e\n\n\u003ch2\u003eWhy Choose FULLERKREG?\u003c\/h2\u003e\n\u003cul\u003e\n  \u003cli\u003e🏭 \u003cstrong\u003eDirect manufacturer\u003c\/strong\u003e — factory in China, no middlemen\u003c\/li\u003e\n  \u003cli\u003e📐 \u003cstrong\u003eStrict DIN dimensional control\u003c\/strong\u003e — 100% inspection on critical dimensions and hardness\u003c\/li\u003e\n  \u003cli\u003e🌍 \u003cstrong\u003eGlobal export experience\u003c\/strong\u003e — serving distributors in Europe, North America, Southeast Asia\u003c\/li\u003e\n  \u003cli\u003e📦 \u003cstrong\u003eFlexible MOQ\u003c\/strong\u003e — small trial orders and large bulk shipments both welcome\u003c\/li\u003e\n  \u003cli\u003e📋 \u003cstrong\u003eFull documentation\u003c\/strong\u003e — material certs, hardness reports, salt spray reports, RoHS declarations\u003c\/li\u003e\n  \u003cli\u003e⚡ \u003cstrong\u003eFast lead times\u003c\/strong\u003e — standard sizes in stock, ready to ship\u003c\/li\u003e\n\u003c\/ul\u003e\n\n\u003chr\u003e\n\n\u003ch2\u003eFrequently Asked Questions\u003c\/h2\u003e\n\n\u003cp\u003e\u003cstrong\u003eQ: What is DIN 6798 Form J?\u003c\/strong\u003e\u003cbr\u003e\nA: DIN 6798 Form J is an internal serrated lock washer. The teeth are on the inner diameter and bite into the fastener shank or bolt head underside when tightened, providing mechanical anti-loosening without marking the outer substrate surface.\u003c\/p\u003e\n\n\u003cp\u003e\u003cstrong\u003eQ: Why 65Mn spring steel for serrated lock washers?\u003c\/strong\u003e\u003cbr\u003e\nA: 65Mn achieves 430–510 HV after quench and temper, providing sharp, durable teeth that maintain their bite-in performance under repeated loading. Higher hardness than standard carbon steel ensures the teeth do not deform under tightening torque.\u003c\/p\u003e\n\n\u003cp\u003e\u003cstrong\u003eQ: What is CR3 passivation?\u003c\/strong\u003e\u003cbr\u003e\nA: CR3 refers to trivalent chromium passivation over zinc electroplating. Provides ≥72h NSS corrosion protection without Cr6+. Fully RoHS compliant.\u003c\/p\u003e\n\n\u003cp\u003e\u003cstrong\u003eQ: How is hydrogen embrittlement managed?\u003c\/strong\u003e\u003cbr\u003e\nA: Post-plate baking at 190–220°C for 4–8 hours per ISO 9587 drives off absorbed hydrogen before the zinc coating seals, restoring tooth integrity and spring properties.\u003c\/p\u003e\n\n\u003cp\u003e\u003cstrong\u003eQ: Do you provide material test certificates?\u003c\/strong\u003e\u003cbr\u003e\nA: Yes. Mill certificates, hardness reports, salt spray reports, and RoHS declarations available upon request.\u003c\/p\u003e\n\n\u003chr\u003e\n\n\u003cp\u003e\u003cstrong\u003eFULLERKREG Fasteners\u003c\/strong\u003e — Precision DIN Standard Fasteners, Direct from Manufacturer.\u003cbr\u003e\nFor wholesale inquiries, technical questions, or custom orders, please contact our sales team.\u003c\/p\u003e","products":[],"url":"https:\/\/www.fullerkr.com\/collections\/din-6798j-zinc-internal-serrated-lock.oembed","provider":"Fullerkreg Fasteners","version":"1.0","type":"link"}